机译:有机芯壳腐蚀抑制剂对模拟混凝土孔溶液加固腐蚀性能的影响
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China;
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China|China Vanke CO LTD Shenzhen 518020 Peoples R China;
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China;
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China;
Guangzhou Univ Guangzhou Univ Tamkang Univ Joint Res Ctr Engn St Guangzhou 510006 Peoples R China;
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China;
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China;
South China Univ Technol Sch Mat Sci & Engn Guangzhou 510640 Peoples R China;
Core-shell corrosion inhibitors; Simulated concrete pore solution; EIS; Reinforced concrete; Raman analysis;
机译:咪唑啉季铵盐腐蚀抑制剂存在下钢筋在模拟混凝土孔隙溶液中的腐蚀性能
机译:pH敏感型核壳有机缓蚀剂的制备及其在模拟混凝土孔隙溶液中的释放行为
机译:碳钢内部混合有机缓蚀剂在氯化物污染的模拟混凝土孔隙溶液中的有效性保护性能
机译:油酸钠作为绿色缓蚀剂,用于模拟混凝土孔隙溶液中碳钢的点蚀
机译:模拟孔溶液中低碳钢增强腐蚀缓蚀剂的研究
机译:新型耐腐蚀钢筋在含氯混凝土孔隙溶液中的点蚀行为
机译:模拟现场服务环境下有机缓蚀剂对混凝土桥梁结构钢筋腐蚀的影响分析
机译:腐蚀抑制剂和环氧涂层增强钢在模拟混凝土孔隙水溶液中的防腐性能