Role of TiO_2 on the densification of zero cement Al_2O_3-MgO spinel castable

摘要

Al_2O_3-MgO spinel castable consisting of 70% Al_2O_3 and 30% MgO was synthesized using raw materials like fused alumina and dead burnt magnesia of different grain sizes. Co-precipitated aluminium hydroxide and magnesium hydroxide gel were used as binder of the castable. Role of TiO_2 additives in different proportions on the densification behaviour of such castable was assessed through the measurement of parameters like bulk density, volume shrinkage, apparent porosity, specific gravity and the microstructure was evaluated by SEM and XRD studies. It was observed that TiO_2 exhibited positive influence on the densification behaviour of these compacts.%Refrattari non formati a base di spinello Al_2O_3-MgO (composizione 70% di Al_2O_3 e 30% di MgO) sono stati sintetizzati a partire da materie prime quali allumina fusa e magnesite cotta a morte con diversa granulometria, adottando come legante gel coprecipitato di Al(OH)_3-Mg(OH)_2. Si è determinato il ruolo degli additivi di TiO_2 in diverse quantità sul comportamento durante densificazione di tali refrattari non formati, mediante la misura di parametri quali densità apparente, ritiro volumetrico, porosità apparente, peso specifico e valutazione microstrutturale, utilizzando la microscopia elettronica a scansione (SEM) e la diffrattometria a raggi X (XRD). Si è osservato che la titania influisce positivamente sulla densificazione dei materiali in esame.