IRON REDOX EQUILIBRIUM AND DIFFUSIVITY IN MIXED ALKALI-ALKALINE EARTH-SILICA GLASS MELTS

摘要

Dependence of redox behavior and diffusivity of iron on temperature and composition was studied in mixed alkali-alkaline earth-silica glass melts by means of square wave voltammetry (SWV). The voltammograms showed that irrespective of K_2O/(Na_2O+K_2O) the peak potential due to Fe~(3+)/Fe~(2+) moved toward negative direction with temperature decrease and the peak current showed a strong dependence on frequency at constant temperature. Iron diffusion coefficient versus melt viscosity showed a good linearity. The compositional dependence showed that the peak potential shifted to the positive direction with increase of K_2O but a typical mixed alkali effect occurred in iron diffusion either at constant temperature or at constant viscosity.