К ВОПРОСУ ОБЕСПЕЧЕНИЯ ВЫСОКОЙ ЭКСПЛУАТАЦИОННОЙ СТОЙКОСТИ ДЕТАЛЕЙ МАШИН

摘要

Made from various types of work pieces and containing carbon in the range of 0,20-0,55 % steel products properties comparative data are shown. The benefit of deformed semi-finished steel product than casted one is shown. The relation between the steel 40H impact toughness magnitude and the degree of its deformation in the hot state is founded. The relation between the steel hardenability with a hardness value in the core of the tooth parts and fatigue-flexural resistance gear is shown. Non-metallic inclusions and steel high hardenability for parts properties negative influence is shown. To stabilize the structure and hardness of steel semi-finished products the heat treatment technology is proposed. To increase while using parts resistance the steel hardenability reglamentation, stable structure and properties hot-deformed semifinished products using, different origin defects using exclusion is recommended.%Приведены сравнительные данные по свойствам стальных изделий, изготовленных из различных видов заготовок и содержащих углерода в пределах 0,20-0,55% Показано преимущество деформированных стальных полуфабрикатов перед литыми. Установлена связь между величиной ударной вязкости стали 40Х и степенью ее деформации в горячем состоянии. Представлена связь прокаливаемоcти стали с величиной твердости в сердцевине зуба детали и усталостно-изгибной стойкостью шестерни. Показано негативное влияние неметаллических включений и высокой прокаливаемоcти стали на свойства деталей. Для стабилизации структурного состояния и твердости стальных полуфабрикатов предложена технология термической обработки. Для повышения стойкости деталей в эксплуатации рекомендовано регламентировать прокаливаемость стали, использовать го-рячедеформированные полуфабрикаты со стабильной структурой и свойствами и исключить использование стали с дефектами различного происхождения.