DESTRUCTION OF WATERPROOFING MEMBRANE ON THE VIADUCT DECK DUE TO BLISTERS CONTEINING HYDROGEN

摘要

Many millions of cubic meters of concrete modified with silica fume have been placed over the years. Moreover high performance concrete (hpc) does not exist without microsilica additive. The advantage of the use of silica fume in concrete technology is described in many papers. In the initial stage of development of hpc technology the negative consequences of silica fume usage was not discussed. However with time such symptoms occurred. Among others concern has been raised over possible risks of hydrogen formation due to free silicon (Si) contained in silica fume. Phenomenon turned out thermodynamically possible and appeared as significant in engineering practice. Paper presents a case study when hydrogen has been detected in blisters of bituminous waterproofing membranes on the viaduct deck made of high performance concrete.%Przez lata wykonano i wbudowano z sukcesem wiele milionów metrów sześciennych betonu modyfikowanego pyłem krzemionkowym. Beton wysokiej wartości (hpc) nie istnieje bez dodatku mikrokrzemionki. Korzyści jakie wynikają ze stosowania pytu krzemionkowego opisano w wielu publikacjach. W początkowym etapie rozwoju technologii betonu hpc nie rozważano negatywnych skutków stosowania pyłu krzemionkowego. Jednakże z upływem czasu pojawiły się takie symptomy. Między innymi stwierdzono możliwość wystąpienia ryzyka tworzenia się wodoru, powodowanego obecnością wolnego krzemu (Si) w pyle krzemionkowym. Występowanie zjawiska okazało się termodynamicznie prawdopodobne i ujawniło swe znaczenie w praktyce inżynierskiej. W artykule przedstawiono analizę przypadku wydzielania wodoru jako przyczynę bardzo intensywnego spęcherzenia przeciwwodnej izolacji bitumicznej na betonowej płycie estakady wykonanej z betonu wysokiej wytrzymałości.