Room temperature soft chemical route for nanofibrous wurtzite ZnO thin film synthesis

摘要

Room temperature soft chemical deposition route has been utilized to grow thin films of ZnO on glass substrate. Annealing at 673 K removed zinc hydroxide phase and nanofibrous ZnO films with wurtzite crystal structure were obtained. Decrease in the room temperature electrical resistivity from 10~7 to 10~4 Ω cm was observed after annealing. The nanofibrous ZnO thin films were sensitive to the explosive liquefied petroleum gas (LPG) and the maximum response of 17% at 698 K under the exposure of 6500 ppm of LPG was obtained.