Control of laser-ablated aluminum surface wettability to superhydrophobic or superhydrophilic through simple heat treatment or water boiling post-processing

摘要

Graphical abstractDisplay OmittedHighlights•Superhydrophilic/superhydrophobic Al surfaces were made by laser ablation and simple post process.•Laser-ablated Al surface became superhydrophobic using heat treatment.•Laser-ablated Al surface became superhydrophilic using boiling water treatment.•Mechanism of wettability change to superhydrophobic/superhydrophilic was explained.•The performances of superhydrophobic and superhydrophilic Al were demonstrated.AbstractRecently, controlling the wettability of a metallic surface so that it is either superhydrophobic or superhydrophilic has become important for many applications. However, conventional techniques require long fabrication times or involve toxic chemicals. Herein, through a combination of pulse laser ablation and simple post-processing, the surface of aluminum was controlled to either superhydrophobic or superhydrophilic in a short time of only a few hours. In this study, grid patterns were first fabricated on aluminum using a nanosecond pulsed laser, and then additional post-processing without any chemicals was used. Under heat treatment, the surface became superhydrophobic with a contact angle (CA) greater than 150° and a sliding angle (SA) lower than 10°. Conversely, when immersed in boiling water, the surface became superhydrophilic with a low contact angle. The mechanism for wettability change was also explained. The surfaces, obtained in a short time with environmentally friendly fabrication and without the use of toxic chemicals, could potentially be applied in various industry and manufacturing applications such as self-cleaning, anti-icing, and biomedical devices.