Thermal characterization of a montmorillonite, modified with polyethylene-glycols (PEG1500 and PEG4000), by in situ HT-XRD and FT IR: Formation of a high-temperature phase

摘要

Two polyethylene-glycols (PEG), having different molecular weight (i.e. PEG 1500 and PEG 4000) were intercalated inside the interlayer space of a STx montmorillonite. The microstructure of the intercalated clay mineral was investigated by thermogravimetry (TG) and in situ high temperature-XRD, in order to assess the evolution of the interlayer space upon temperature. Data were collected over a temperature range of 25-1000℃ and 25-850 X for TG and thermo-XRD, respectively. Decomposition of the intercalated polymers was very different compared to the one of the pure surfactants, as detected by TG and FT IR spectroscopy. In situ high temperature-XRD data showed the formation of a high-temperature phase, detected at 250℃, independently from the molecular weight of the PEG intercalated. This phase showed to be stable when the temperature was decreased to 25℃ and was raised again to 250℃. An irregularly interstratified phase was observed when the modified clay minerals were heated at 200℃.