Nanomechanical Properties of Different Dental Restorative Materials

摘要

The aim of this study is to determine the hardness and roughness of glass ionomer cement, glass carbomer, and compomer by nanoindentation. Three different dental restorative materials: glass ionomer cement, glass carbomer cement, and compomer were used. Disc specimens (1 0 mm x 1 mm) were prepared from each material using teflon mold. All specimens were light cured according to the manufacturer's instructions. The specimens were then mounted in polyacrilic resin. After grinding and polishing the specimens were stored in distilled water at 37 degrees C for 1 day. The specimens were investigated using nanoindenter. The highest nanohardness was measured for glass ionomer cement and the lowest for glass carbomer. Regarding roughness, glass ionomer cement and compomer showed the highest mean values. Glass ionomer cement and compomer exhibited similar nanomechanical properties. Glass carbomer had superior ability to be polished up.