The effect of recovery time and test conditions on viscoelastic measures of tensile damage in cortical bone

摘要

Stiffness degradation and strength degradation are often measured to monitor and characterize the effects of damage accumulation in bone. Based on evidence that these properties could be affected by not only damage magnitude but also test conditions the present study investigated the effect of hold condition and recovery time on measures of tensile damage.Machined human femoral cortical bone specimens were subjected to tensile tests consisting of a pre-damage diagnostic loading cycle, a damage loading cycle and post-damage cycle. Controlled variables were recovery time (1, 10, 100 minutes) and hold condition (zero load or zero strain) after the damage cycle. Damage measures were calculated as the ratio of each post-damage cycle to the pre-damage value for loading modulus, secant modulus, unloading modulus stress relaxation and strain (stress) recovery at 1 minute post-diagnostic time.The damage cycle caused reductions in all measures and some measures varied with recovery time and hold condition. Apparent modulus degradation for both hold conditions decreased with recovery time. Stress relaxation was unaffected by recovery time for both hold conditions. Zero-strain hold conditions resulted in lower values for degradation of modulus and change of relaxation. Stress or strain recovery after the damage cycle was evident through 100 minutes, but 90% of the recovery occurred within 10 minutes. The results demonstrate that choice of test conditions can influence the apparent magnitude of damage effects. They also indicate that 10 minutes recovery time was sufficient to stabilize most measures of the damage state.