Strength retention behavior of oriented PLLA 96L/4D PLA and 80L/20DL PLA

摘要

The strength retention characteristics of oriented semicrystalline polylactides were monitored during hydrolytic degradation in vitro. The effects of the polymer type, the material’s initial inherent viscosity (iv), the sample diameter and the residual monomer content on strength retention were analyzed. The analyzed polylactides had similar, but not identical, strength retention characteristics. It was concluded that a higher degree of initial crystallinity was a major variable determining the earlier and more profound strength loss of PLLA than 96L/4D PLA and 80L/20 D,L PLA. Samples with a higher initial iv were found to have a longer strength retention time than lower iv samples. Size-dependency was observed, as the strength retention time was shorter for the smaller diameter samples. This size-dependency was caused by faster iv decay. The amount of residual monomer content had a remarkable impact on strength retention. Neither the sample diameter, initial iv or residual monomer content were found to have an effect on the iv range in which there was a rapid decline in strength properties. Therefore, it was concluded that the inherent viscosity and/or molecular weight of oriented PLLA, 96L/4D PLA and 80L/20 D,L PLA is a major variable determining the strength retention of these materials.