Effect of Fe_(3)O_(4) nanoparticles on magnetic xerogel composites for enhanced removal of fluoride and arsenic from aqueous solution

摘要

Fe_(3)O_(4)magnetic xerogel composites were prepared by polycondensation of resorcinol(R)-formaldehyde reaction via a sol-gel process in an aqueous solution through varying the molar ratio of Fe_(3)O_(4)nanoparticles(MNPs),catalyst(C),and water(W)content.MNPs were obtained by co-precipitation(MC),oxidation of iron salts(MO),or solvothermal synthesis(MS).Both MNPs and magnetic xerogels were examined regarding the performance of arsenic and fluoride removal in a batch system.The MC-based MNPs had higher adsorption capacities for both fluoride(202.9 mg/g)and arsenic(3.2 mg/g)than other MNPs in optimum conditions.The X-ray diffraction,Fourier transform infrared spectroscopy,and energy-dispersive X-ray spectroscopy confirmed that Fe was composed into the polymeric matrix of magnetic xerogels that contained 0.59%-4.42%of Fe with a molar ratio of MNPs(M)to R between 0.01 and 0.10.With low R/C and optimum M/R ratios,an increase in the surface area of magnetic xerogels affected the fluoride and arsenic adsorption capacities.The magnetic xerogel composites with the MC-based MNPs prepared at a fixed R/C ratio(100)and at different R/W(0.05-0.06)and M/R(0.07-0.10)ratios had a high arsenic removal efficiency of 100%at an As(V)concentration of 0.1 mg/L and pH of 3.0.The maximum adsorption capacities of magnetic xerogels were approximately five times higher than those of the xerogels without MNP composites.Therefore,Fe_(3)O_(4)nanoparticles enhanced the adsorption of arsenate and fluoride.The variations of alkaline catalyst and water content significantly affected the resulting properties of textural and surface chemistry of magnetic xerogel composites.