A γ-TiAl base alloy with the composition of Ti-34Al-2Mn（wt--%）was prepared by consum-able electrode arc-melting technique.The effect of homogenization processing following arc-melt-ing on its microstructure and mechanical properties was investigated.The emphases were placedon the microstructural evolution during solidification and homogenization,and the relationship be-tween microstructure and ductility.It has been determined that the samples annealed at 900℃for 20 h exhibit the best ductility compared with those treated at other temperatures up to 1100℃,and they have a mixed structure of equiaxed grain of γ-TiAl single phase and some prima-ry lamellar grains which include three types of interfaces,i.e.,α2/γ,/γ/γS,γ/γT,maintainingspecific orientaion relationships between both sides.The ductility improvement is believed to be as-sociated with existence of suitable amount of α2-Ti3Al phase and the refinement of grains ob-tained at 900℃.