Characterization of anodic coating formed on Mg-3Nd-0.2Zn-0.4Zr Mg alloy in alkaline electrolyte

摘要

Anodization of rare earth-containing Mg alloy of Mg-3Nd-0.2Zn-0.4Zr(mass fraction,%)(NZ30K) was performed in composite electrolyte containing NaOH,KOH,K_2SiO_3,Na_2SiO_3,NaF,KF etc.The anodic coating was characterized by using X-ray diffraction(XRD),field emission electron scanning mieroscope(FE-SEM) and electron probe microscopic analysis(EPMA).The corrosion resistance of the anodized alloy and the substrate was evaluated in 5%NaCl solution using electrochemical impedance spectroscopy(EIS).The results of XRD show that the anodic coating is mainly composed of MgO.EPMA indicates that magnesium and oxygen are almost uniformly distributed across the coating,and the fluorine content decreases gradually from the interface of coating-substrate to the surface,whereas the distribution of silicon is reverse to that of fluorine.The results of EIS analysis shows that the anodic coating exhibits the superior corrosion resistance for NZ30K alloy.