aluminum alloy was implanted with nitrogen then titanium at different titanium target sputtering currents by plasma-based ion implantation(PBII). The appearances were observed by atomic force microscope, and the surface hardness was measured with Knoop hardness tester and the mechanical property microprobe. Ball-on-disc dry wear experiments were performed under ambient air conditions, to study the tribological properties of the modified layers against GCr15 steel ball, employing various loads and a constant sliding speed. After dual modifications, surface hardness at 100 nm depth could reach to 9 GPa, increasing by about 5 times; tribological properties at lower load(e.g. 1 N) were obviously improved, with the friction coefficient(below 0.2) decreasing by over 60%, and the wear life(800 times) increasing by about 5 times. Meanwhile, with the increase of the sputtering current, the appearance is smooth, the surface hardness tends to a slow and even variation, the wear life presents a parabola-like change, and the friction coefficient and the adhesive wear degree decrease. However, tribological properties are reduced with the increase of the load due to the modified layer rapidly getting thin.
展开▼