Three-dimensional silica fiber reinforced silicon nitride based composites were fabricated by preceramic polymer infiltration and pyrolysis method using perhydropolysilazane as a precursor. The effects of precoating and high temperature calcination on the microstructures of the composites were investigated by scanning electron microscopy. For the composite without a precoating, the fracture surface is plain, and the fiber/matrix interfaces become very unclear after calcination at 1 600 ℃ due to intense interfacial reactions. The composite with a precoating shows tough fracture surface with distinct fiber pull-outs, and the fiber/matrix interfaces are still clear after calcination at 1 600 ℃. It is the appropriate precoating process that contributes to the good interfacial microstructures for the composite.