正火预处理对调质26CrMoV钢Φ195 mm棒材横向-20°C冲击功的改善

摘要

对直径为Φ195 mm的Ti-V微合金化26CrMoV钢(/％:0.27C,0.45Mn,0.25Si,0.006P,0.004S,0.97Cr,0.78Mo,0.002Ti,0.043V)热轧棒材取样后在热处理试验室分别按880°C淬火+645°C回火和925°C正火+880°C淬火+645°C回火两种工艺进行热处理.通过检测其皮下25.4 mm处力学性能,发现两种热处理工艺试样的屈服及抗拉强度相近,淬火+回火处理的-20°C横向冲击功为46～47 J,而正火+淬火+回火处理的-20°C横向冲击功为79 ～86 J,改善效果明显.对比观察发现经正火预处理后钢的回火索氏体及铁素体组织更加均匀、细小.