Electrochemical and microstructural characterization of cyclic redox behaviour of SOFC anodes

摘要

The oxidation of Ni to NiO in solid oxide fuel cell (SOFC) anode will result in large bulk volume change, which may change the interfaces of the two phases in the anode cermet and thus may cause significant performance degradation. The reduction and oxidation (redox) of the Ni/YSZ cermet were studied at 800 ℃. Anodic polarization measurements were performed before and after redox cycles. The anode current density at an overpotential of 100 mV kept decreasing during the whole redox treatment. It decreased from 19.11 to 7.95 mA·cm-2 after two redox cycles. Anode supported unit cell was assembled for cell′s discharge measurements. Cell performance declined after each redox cycle. The maximum power density decreased from 126.28 to 40.32 mW·cm-2. The microstructural changes after redox cycling were recorded using scanning electron microscopy (SEM). The results reveal that after re-oxidation, the Ni gets coarse and has a higher porosity; the nickel network structure turns to be desultory.