Oxidation behavior of Nb–24Ti–18Si–2Al–2Hf–4Cr and Nb–24Ti–18Si–2Al–2Hf–8Cr hypereutectic alloys at 1250°C

摘要

Nb-24Ti-18Si-2Al-2Hf-4Cr and Nb-24Ti-18Si-2Al-2Hf-8Cr alloys were prepared by arc melting in a water-cooled crucible under argon atmosphere.Microstructural characteristics and oxidation resistance of the alloys at 1250 ℃ were investigated.The results show that,when the Cr content is 4 at%,the microstructures consist of(Nb,Ti)_(ss) and Nb_5Si_3;as Cr content increases to8 at%,C14 Laves phase Cr_2Nb is formed.The isothermal oxidation tests show that the oxidation kinetics of the two alloys follow similar features.The weight gains of the two alloys after oxidation at 1250℃ for 100 h are 235.61 and198.50 mg·cm^(-2),respectively.During oxidation,SiO_2,TiO_2,Nb_2O_5 and CrNbO_4 are formed at first.Then,Ti_2Nb_(10)O_(29) is formed after oxidation for 20 min and begins to change into TiNb_2O_7 as the oxidation proceeds.SiO_2 is formed as solid state at first but later evolves into glassy state to improve the cohesion of the scale.After oxidation for 100 h,oxidation products consist of SiO_2,TiNb_2O_7,Nb_2O_5 and CrNbO_4.