Friction stir welding was applied to Ti-6 A1-4 V plates with 5 mm in thickness.The microstructure and mechanical properties were investigated.A full lamellar microstructure was developed near the top surface,and the size of priorβgrain gradually decreases as the distance from the top surface increases.The microstructure of the bottom is fine equiaxed a grains,and the mean size is2μm.A mixture microstructure consisting of primary a,lamellarα+βand fine equiaxedαis discovered in thermomechanically affected zone(TMAZ).Results of transverse tensile test show that the tensile strength of the joint reaches 98%that of the base material(BM).Quasi-static compression test shows that the joint exhibits larger compressive strength and failure strain than the BM.Dynamic compressive strength of the joint is close to that of the BM;furthermore,the strain at the peak stress and energy absorption of the joint are larger than those of the BM.
展开▼
机译:平成28年度论文赏受赏轮文:Effect of Si/Fe Composition, Substrate Temperature, and Substrate Orientation on the Structure and Magnetic Properties of Fe-Si Alloy Film