Hybrid mesoporous polystyrene-silica materials were successfully prepared through HCl-catalyzed sol-gelreactions of tetraethyl orthosilicate (TEOS) and triethoxysilyl-functionalized polystyrene obtained via atom transfer radicalpolymerization (ATRP) of styrene, in the presence of citric acid (CA) as non-surfactant template or pore-forming agent andfollowed by ethanol extraction to remove template molecules. The materials were characterized by infrared spectroscopy(IR), N2 adsorption-desorption measurements, powder X-ray diffraction (XRD), thermogravimetric analysis (TGA) andtransmission electron microscopy (TEM). The results indicate that the materials prepared with 50 wt%-60 wt% templatecontents have average pore size s of 2-3 nm and large surface areas (ca. 886 m2/g) as well as high pore volumes (ca.0.53 cm3/g). The mesoporosity arises from interconnected channels and pores with disordered arrangements. The porediameters and pore volumes increase as the template content is increased. The pore diameters show a little change uponheating at 200℃ overnight. However, the materials do not have good hydrothermal stability.
展开▼