Synthesis and Properties of High Performance Functional Polyimides Containing Rigid Nonplanar Conjugated Fluorene Moieties

摘要

A diamine(WuFDA) containing vertical rigid non-planar conjugated fluorene moiety and low polarizability group(C―F)was designed and synthesized through three steps of reactions(halogenated reaction, Suzuki coupling reaction, and reduction reaction).Four kinds of high performance functional polyimides(WuFPI-6 F, WuFPI-BP, WuFPI-BT, and WuFPI-PM) were thus prepared by the condensation polymerization of WuFDA with four commercial dianhydride 6 FDA, BPDA, BTDA, and PMDA, respectively. The polyimides exhibited low dielectric constant, excellent thermal stability, outstanding solubility, good film-forming property, and mechanical properties. The dielectric constants of the polyimides were in the range of 2.28-2.88(f = 10~4 Hz). The 5% weight-loss temperatures(Td 5%)in nitrogen were in the range of 555-584 °C, and the glass transition temperatures(T_g) were in the range of 408-448 °C. The weight loss of WuFPI-BP maintaining at 450 and 500 °C for half an hour was only 0.33% and 1.26%, respectively. All the WuFPIs could be dissolved in almost all organic solvents, even chloroform. The tensile strength and tensile modulus of these films were in the ranges of 78.6-85.7 MPa and 3.1-3.2 GPa, respectively. In addition, the polyimides displayed light color with special fluorescent and resistive switching(ON-OFF) characteristics; the maximum fluorescence emission was observed at 422-424 nm in NMP solution and at 470-548 nm in film state. The memory devices with the configuration of indium tin oxide/WuFPIs/aluminum(ITO/WuFPIs/Al) exhibited distinct volatile memory characteristics of static random access memory(SRAM), with an ON/OFF current ratio of 10~5-10~6. These functional polyimides showed attractive potential applications in the field of high performance flexible polymer photoelectronic devices or polymer memory devices.