This work described the preparation of easily colored meta-aramid(PMIA) copolymers from m-phenylenediamine(MPD),isophthaloyl dichloride(IPC), and 3,4′-oxydianiline(3,4′-ODA) via solution polycondensation in N,N-dimethylacetamide(DMAc). The novel co-PMIAs were obtained in relatively high inherent viscosities ranging from 1.32 dL/g to 2.53 dL/g, which could be easily cast into flexible films with high transparence or spun into fibers. All the newly synthesized copolymers possessed excellent thermal stabilities even better than that of commercial PMIA, with 5% weight loss temperatures higher than 430 °C in nitrogen measured by TGA and glass transition temperature of 267–277 °C measured by DSC. The cast films exhibited good mechanical properties with a tensile strength up to107 MPa and a tensile modulus up to 2.2 GPa. The resultant PMIAs also showed good solubility and better dye ability for cationic dyes.
展开▼
机译:Synthesis and Characterization of L-Lysin Coated Iron Oxide Nanoparticles as Appropriate Choices for Cell Immobilization and Magnetic Separation | Bentham Science.
机译:preparation and characterization of imidazolium-functionalized poly (ether sulfone) as anion exchange membrane and ionomer for fuel cell application