Facile synthesis of high electrical conductive CoP via solid-state synthetic routes for supercapacitors

摘要

Co-P precursor was prepared by a mechanical alloying method and then is controlled to synthesis of Co P phase through an annealing method. The optimal conditions of ball milling and annealing temperature are investigated. The Co P exhibits higher electrical conductivity than graphite and cobalt oxide, showing excellent pseudocapacitive properties due its high electrical conductivity which can result in a fast electron transfer in high rate charge–discharge possess. The as-obtained Co P electrode achieves a high specific capacitance of 447.5 F/g at 1 A/g, and displays an excellent rate capability as well as good cycling stability. Besides, the asymmetric supercapacitor(ASC) based on the Co P as the positive electrode and activated carbon(AC) as the negative electrode was assembled and displayed a high rate capability(60%of the capacitance is retained when the current density increased from 1 A/g to 12 A/g), excellent cycling stability(96.7% of the initial capacitance is retained after 5000 cycles), and a superior specific energy of19 Wh/kg at a power density of 350.8 W/kg. The results suggest that the Co P electrode materials have a great potential for developing high-performance electrochemical energy storage devices.