Interfacial toughness evaluation of thermal barrier coatings by bending test

摘要

Determining the interfacial properties of thermal barrier coatings(TBCs) is imperative for their durability evaluation and further improvements. A ceramic coating(topcoat) and a NiCoCrALY bondcoat were atmospheric-plasma-sprayed(APS) on a stainless steel substrate. A modified three-point bending test was adopted to initiate and propagate the topcoat/bondcoat(TC/BC)interfacial crack. After a complete delamination, the fracture surfaces were examined by an optical microscope, which shows that the cracking plane was merely on the TC/BC interface. Based on the experimental results of load–displacement and crack length–displacement,the strain energy release rate G for crack propagation was calculated, and the averaged magnitude was 77.1 J/m^2.Repeatable results have indicated that the method can be used for the evaluation of interfacial fracture toughness in thermal barrier coatings and other multi-layer structures.