Systematically describes the crux-tackling achievements in silkcrease and shri n k resistant finishing technology. High temperature and pressure rapid scouring can improve silk dry and wet wrinkle recovery by about 10 degrees. For better r esults, different compound finishing technologies with composite finishing agents, various crease and shrink resistant finishing agents should be adopted. It i s found that the finished Crepe de Chine 12102 reaches 300 degrees in dry crease recovery, over 265 degrees in wet crease recovery, and below 3% in shrinkage.%系统地叙述了真丝绸防缩抗皱整理技术的攻关成果,采用高温高压快速精练工艺,真丝绸干、湿弹性回复角提高10°左右;真丝绸要取得较好的干、湿弹效果,必须采用复合型整理剂;采用不同类型防缩抗皱整理剂、不同工艺进行复合整理,12102双绉干弹回复角达到300°,湿弹回复角达到265°以上,缩水率降至3%以下。