The Cracking Induced by Oxidation-Hydriding in Welding Joints of Zircaloy-4 Plates

摘要

The welding joints of Zircaloy 4 plates obtained by diffusion welding at 800°C under pressure in vacuum were cracked during autoclave tests at 400°C superheated steam after exposure longer than 150 days. The section of specimens was examined by optical microscopy and the composition at the tips of cracking was analyzed by electron microprobe. The result shows that the combination of oxidation and hydriding induced cracking is responsible for this failure of the welding joints.