Tailoring Texture to Highly Strengthen AZ31 Alloy Plate in the Thickness Direction via Pre-tension and Rolling-Annealing

摘要

Conventional wrought Mg alloys,such as AZ31 and ZK60 rolled plates,usually exhibit significantly low tensile yield strength in the thickness direction.This can be attributed to the high activity of{10-12}tension twinning due to the strong basal texture(//ND,normal direction).In this work,the tensile yield strength in the ND of the as-rolled(AR)AZ31 plate increased from 50 to 150 MPa(increased by 200%)via simple processing,i.e.,pre-tension and rolling-annealing(PTRA)treatment.The strong basal texture(//ND)of the AR plate was changed into a weakened fiber texture(⊥ND).The evolution of microstructures during PTRA treatment and the activated deformation modes during uniaxial tension were studied quantitatively and statistically by the means of intergranular misorientation(IM)and in-grain misorientation axes(IGMA)analysis.The results indicate that various twin variants,as well as{10-12}-{10-12}secondary twins,were activated during pre-tension and rolling,and most residual matrix was consumed by twins after annealing.The dominated deformation modes in tension changed from{10-12}tension twinning(the AR sample)to prismatic slip(the PTRA sample)in the early tensile deformation.The underlying formation mechanism of the fiber texture and corresponding strengthening mechanism were discussed.