Microstructure Evolution and Microhardness of Ultrafine-grained High Carbon Steel during Multiple Laser Shock Processing

摘要

Surface microstructure and microhardness of(ferrite+cementite)microduplex structure of the ultrafinegrained high carbon steel after laser shock processing(LSP)with different impact times were investigated by means of scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray diffraction(XRD)and microhardness measurements.Equiaxed ferrite grains were refined from 400 to 150nm,and the cementite lamellae were fully spheroidized,with a decrease of the particle diameter from 150 to 100nm as the impact times increased.The cementite dissolution was enhanced significantly.Correspondingly,the lattice parameter ofα-Fe and microhardness increased with the impact times.