Glass forming ability of Zr-and Fe-based alloys at quenching from melts

摘要

The master alloy ingots (MAI) with the nominal composition Zr 52.5 Ti 5Cu 17.9 Ni 14.6 Al 10 and Fe 61 Co 7Zr 10 Mo 5W 2B 15 (at%) were prepared by arc melting in Ti gettered Ar atmosphere. The Zr based buttons of 6 mm and 9 mm in diameter were fully amorphous, but those of 13 mm in diameter experienced crystallization. The glass forming ability (GFA) of Fe based alloys was relatively lower, and the buttons obtained were fully crystallized. The microhardness of the Zr based buttons was about 500(Hv), and the Fe based rod obtained by injection technique exhibited a high Vickers hardness of 1329. In addition, an amorphous crystalline transition layers were observed in both the buttons and the rods.