In-plane Tensile Behaviors of Bi-axial Warp-Knitted Composites under Quasi-static and High Strain Rate Loading

摘要

The in-plane tensile behaviors of bi-axial warp-knitted(BWK) composites under quasi-static and high strain rates loading were experimentally analyzed in this article. The tensile tests were conducted along warp direction( 0°) and weft direction( 90°) at quasi-static rate of 0. 001 s^(-1) and high strain rates ranging from 1 450 to 2 540 s^(-1),respectively. It is found that the significant strain rate sensitivity can be observed in the stress-strain curves of BWK composites. The fracture morphologies of BWK composites demonstrate that the tensile failure modes are shear failure and fiber breakage under the quasi-static testing condition while interface failure and fibers pullout are at high strain rates.