Flame retardancy and its mechanism of polymers flame retarded by DBDPE/Sb2O3

摘要

The flammability characterization and thermal composition of polymers flame retarded by decabromodiphenylethane(DBDPE) and antimony trioxide (Sb2O3) were studied by cone calorimeter and thermogravimetry (TG). The results show thatABS/DBDPE/Sb2O3 has the similar flammability parameters and thermal composition curves to ABS/DBDPO/Sb3O3. It suggests thatDBDPE/Sb2O3 has the similar flame retardant behavior to DBDPO/Sb2O3. The heat release rate (HRR) and the effect heat combustion (EHC) curves of polymers flame retarded by DBDPE/Sb2O3 all decrease, but the mass loss rate (MLR) curve slightly increase. It shows that the decrease of HRR is not due to the increase of char formation ratio but the generation of incombustible gases. The major flame retardant mechanism of DBDPE/Sb2O3 is gas phase flame retardant mechanism. Increasing content of Sb2O3in DBDPE/Sb2O3 can improve the flame retardant property and thermal stability of aerylonitrile butadiene styrene. Sb203 has a good synergistic effect with DBDPE.