Investigation of tribological characteristics of nickel alloybased solid-lubricating composites at elevated temperatures under vacuum

摘要

The development of a high‐performance solid‐lubricating composite with excellent self‐lubricity over a broad temperature range in vacuum is significant to solve the frictional problems of spatial mechanisms.In this study,the vacuum tribological behaviors of nickel‐matrix/Ag/(Ca,Ba)F2/graphite(0–2 wt%)composites were studied from 25 to 800°C.The results show that the synergistic effects of solid lubricants can significantly improve the tribological properties of the composites in vacuum,with the graphite content contributing considerably.For 2 wt%graphite,a low friction coefficient(0.14–0.25)and the lowest wear rate((0.12–4.78)×10^(-5) mm^(3)∙N^(-1)∙m^(-1))were observed in vacuum over the entire testing temperature range.Moreover,the wear mechanisms were clarified via analysis of the chemical composition and morphologies of the sliding surfaces.