Fabrication and properties of silver-based composites reinforced with carbon-coated Ti_(3)AlC_(2)

摘要

Ti_(3)AlC_(2)-reinforced Ag-based composites,which are used as sliding current collectors,electrical contacts,and electrode materials,exhibit remarkable performances.However,the interfacial reactions between Ag and Ti_(3)AlC_(2) significantly degrade the electrical and thermal properties of these composites.To diminish these interfacial reactions,we fabricated carbon-coated Ti_(3)AlC_(2) particles(C@Ti_(3)AlC_(2))as reinforcement and prepared Ag–10wt%C@Ti_(3)AlC_(2) composites with carbon-layer thicknesses ranging from 50–200 nm.Compared with the uncoated Ag–Ti_(3)AlC_(2) composite,Ag–C@Ti_(3)AlC_(2) was found to have a better distribution of Ti_(3)AlC_(2) particles.With increases in the carbon-layer thickness,the Vickers hardness value and relative density of Ag–C@Ti_(3)AlC_(2) gradually decreases.With a carbon-layer thickness of 150 nm,we obtained the lowest resistivity of Ag–C@Ti_(3)AlC_(2) of 29.4135.5×10^(−9)Ω·m,which is half that of Ag–Ti_(3)AlC_(2)(66.7×10^(−9)Ω·m).The thermal conductivity of Ag–C@Ti_(3)AlC_(2) reached a maximum value of 135.5 W·m^(−1)·K^(−1) with a 200-nm carbon coating(~1.8 times that of Ag–Ti_(3)AlC_(2)).These results indicate that the carbon-coating method is a feasible strategy for improving the performance of Ag–C@Ti_(3)AlC_(2) composites.