Effect of Alumina Particles Addition on Physico-Mechanical Properties of AL-Matrix Composites

摘要

Metal-matrix composites (MMCs) are attracting considerable interest worldwide because of their superior mechanical and tribological properties. This study describes multifactor-based experiments that were applied to research and investigates Aluminum matrix composite reinforced with 5, 10 & 15 wt% Alumina particles. Mechanical mixing technique was used for fabrication. Sintering was carried out in a vacuum furnace at 600°C for 1 hr. The effects of Alumina percentage on the density, microstructure, both electrical & thermal conductivities, hardness and compression strength was investigated. The results showed that sample containing 5 wt% Alumina is near-fully dense. Also it has the highest hardness and compression strength.