Microstructure and corrosion resistance of a Mg2Sn-dispersed Mg alloy subjected to pulsed electron beam treatment

摘要

We report that the corrosion resistance of a Mg-Sn-based alloy with MgzSn precipitates can be considerably improved by surface modification using pulsed electron beam treatment.The alloy subjected to a pulse electron beam treatment showed a modified surface layer with a thickness of〜12 μm,appearing more resistant to corrosion attack than the bare surface of the alloy.In 0.6 M NaCl solution,the alloys with and without the surface modification exhibited average corrosion rates of 4.3 and 8.1 mm y^-1,respectively.The improved corrosion resistance was attributed to reduced cathodic activation,resulting from the surficial reduction of relatively noble Mg2Sn precipitates.