Effect of pre-deformation on microstructure and mechanical properties of WE43 magnesium alloy Ⅱ: Aging at 250 and 300 ℃

摘要

In this work,the microstructural evolution and mechanical properties of a pre-deformed WE43 magnesium alloy when aged at 250 and 300℃ were further investigated.It is found that the abundant deformation twins introduced by pre-deformation were maintained within the alloy during the aging treatment.Second particles formed at the twin boundaries and coarsened with aging time,especially at 300℃.When peak-aged at 250℃,the fine metastable β'''and β' precipitates formed in the un-deformed alloy have been transformed into relatively large β1 and β precipitates by the pre-deformation.While peak-aged at 300℃,the pre-deformation obviously refined the β precipitates.Mechanical properties indicate that pre-deformation can increase the yield strength by 19MPa and 54MPa for the peak-aged alloy at 250℃ and 300℃,respectively,and will not obviously deteriorate the tensile elongations.