>Innovative preparation of Co@Cu Fe_(2)O_(4) composite via ball-milling assisted chemical precipitation and annealing for glorious electromagnetic wave absorption
Innovative preparation of Co@Cu Fe_(2)O_(4) composite via ball-milling assisted chemical precipitation and annealing for glorious electromagnetic wave absorption
To deal with the growing electromagnetic hazards,herein a Co@CuFe_(2)O_(4)absorbing agent with excellent impedance matching at thin thickness was obtained via an innovative route of ball-milling assisted chemical precipitation and annealing.The as-prepared composite possesses excellent interface polarization ability due to sufficient contact between CuFe_(2)O_(4)NPs and flat Co,and this compressed Co lamella can also provide sufficient eddy current loss.Moreover,the dipole polarization,electron hopping/conduction,and structural scattering also contribute to the broadband microwave absorption of the composite.Thus,the minimum microwave reflection loss achieves-35.56 d B at12.93 GHz for 1.8 mm thickness,and the broadest efficient absorption bandwidth can reach 6.74 GHz for a thinner thickness of 1.72 mm.The preparation method reported here can be referenced as a new-type route to manufacture electromagnetic absorbers with outstanding performance.
展开▼