首页> 外文期刊>中国物理：英文版 >Self-assembly behaviour of amphiphilic diblock copolymer in selective solvents studied by synchrotron small-angle x-ray scattering
【24h】

Self-assembly behaviour of amphiphilic diblock copolymer in selective solvents studied by synchrotron small-angle x-ray scattering

机译：同步加速器小角X射线散射研究两亲性二嵌段共聚物在选择性溶剂中的自组装行为

获取原文
获取原文并翻译 | 示例
       
页面导航
  • 著录项
  • 相关主题
机译：The aggregation behaviour of styrene-vinyl benzoic acid (PSm-b-PVBAn) amphiphilic diblock copolymers in selective solvents with different m and n was investigated by synchrotron small-angle x-ray scattering (SAXS). We have carried out a detailed analysis of scattering intensity, dimension, shape and microstructure of the diblock copolymers of narrow distribution in water, methanol, ethanol and isopropanol selective solvents, respectively. We have found that the aggregation behaviour of the copolymer depends on the nature of the solvent and the micelle forms fiat disc objects with the ratio of radius ω=0.4. The average radius gyration Rg of the copolymer decreases as solvents change from isopropanol to ethanol and to methanol, and increases with increasing pH in aqueous solution, but decreases with the addition of COCl2 in ethanol solvent. The scattering intensity of diblock copolymer micelle follows I(h) ∝ h-α in different selective solutions, suggesting that the PSm-b-PVBAn coils have self-similar structure behaviour or a fractal structure in the selective solvents. All of these revealed that the aggregation behaviour of the diblock copolymer changes dramatically with experimental condition in the selective solvent. The increase of mass fractal dimension (Dm) from 2.12 to 2.47 indicates that the copolymer chain changes from a swollen coil to a rather compact disc in the course of changing solvents, decreasing surface fractal dimension (Ds) from 2.98 to 2.58 indicates that the copolymer micelle change from a rather rough surface to a smooth form in the course of increasing pH in aqueous solutions, and increasing Dm and Ds from 2.29 to 2.35 and 2.70 to 2.90, respectively, indicates the shrinkage of copolymer micelle to a rather compact and rough disc form by adding COCl2 in ethanol solvents.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号