The influences of deeply overdischarge on the negative electrode alloy of Ni/MH battery were studied. After overdischarge, La(OH) 3 and Al(OH) 3 are found to form in the negative electrode through XRD analysis. The hydrogen storage alloy powder from spent Ni/MH batteries was recovered by chemical and melting method according to degradation mechanism. The structure of recovered alloy was measured by XRD. The experimental results demonstrate that the alloy structure is CaCu 5 type. The constant current charge/discharge test was carried out to the original alloy and the recovered alloy. It is found that their discharge capacities are almost the same, but the discharge potential of the recovered alloy is higher than that of the original alloy. The results of cyclic lifetime test demonstrate that the capacity degradation of the recovered alloy is slower than that of the original one.