Comparison of as-cast microstructure,tensile and creep properties for Mg-3Sn-1Ca and Mg-3Sn-2Ca magnesium alloys

摘要

The as-cast microstructure,tensile and creep properties of Mg-3Sn-1Ca and Mg-3Sn-2Ca magnesium alloys were investigated and compared by using optical microscopy and scanning electron microscopy,X-ray diffraction analysis and tensile tests. The results indicate that the as-cast microstructures of Mg-3Sn-1Ca and Mg-3Sn-2Ca alloys are different.The former is mainly composed ofα-Mg,eutectic CaMgSn and solid state precipitation of Mg 2 Sn,whereas the latter is mainly composed ofα-Mg, primary CaMgSn,eutectic CaMgSn and Mg2Ca phases.As a result,the two alloys obtain different tensile and creep properties. Mg-3Sn-1Ca alloy shows relatively higher ultimate tensile strength and elongation at room temperature and 150℃than Mg-3Sn-2Ca alloy,however,the yield strengths of Mg-3Sn-1Ca alloy at room temperature and 150℃are relatively low.In addition,the creep properties of Mg-3Sn-1Ca alloy at 150℃and 70 MPa for 100 h are obviously lower than those of the Mg-3Sn-2Ca alloy.