Oxidation behaviors of Ni(Cr)-TiB2 coating deposited by HVOF technique were studied at 800,900 and 1 000℃in air. The microstructures of as-sprayed and oxidized coatings were characterized by X-ray diffractometry(XRD)and scanning electron microscopy(SEM).After oxidation at 800℃,a thin and adherent oxide layer was formed on the surface of the coating.With increasing exposure temperature,the thickness of the oxide layer increased;and at 1 000℃the oxide layer separated from the coating.Investigation of the kinetics of oxidation by using the thermogravimetric analysis(TGA)technique shows a parabolic oxidation rate.