Using tabular alumina as aggregate,tabular alumina fines, reactive alumina ultra-fines, aluminum powders,silicon powders,carbon black,flake graphite,B4C and zircon fines as matrix,low carbon Al2O3- C refractories were prepared. Influences of zircon powders additions( 0,3%,5% and 7%,in mass,the same hereinafter) on properties,phase composition and microstructure were investigated. The results show that the ZrO2- nitride can be in-situ formed through carbothermal reduction and nitridation in Al2O3- C refractories.With the increase of zircon powder,the oxidation resistance of the Al2O3- C refractories improves obviously,the oxidized layer thickness decreases from 7. 94 mm without zircon to 2. 71 mm with 5% zircon. HMOR at 1 400 ℃of the Al2O3- C refractories reaches the maximum 14. 9MPa when zircon addition is 5%. With the increase of zircon powder,the apparent porosity and bulk density change a little,CMOR and CCS increase.