Effect of La on yield strength,tensile strength elongation,and impact energy at low temperature (0℃to-60℃) of BT100H steel was studied by mechanical property testing.The results show that,compared with the steel without La,yield strength,tensile strength and elongation of test steel with La increased 6.3 MPa,9.8 MPa and 1%on average,respectively,and impact energy from-60℃to 0℃decreased 33.8%for No.14 steel and 60.7%for steel without La.Effects of La on microstructure inclusion,and original Austenitic grain size of BT100H casing for heavy oil thermal recovery were also investigated by electronic microscopy.TEN,SEM and EDS.