Effect of Cu content on microstructures and mechanical properties of ADI treated by twostep austempering process

摘要

The effect of Cu content on the microstructures and mechanical properties (yield strength, ultimate tensile strength, impact energy, fracture toughness) of austempering ductile iron (ADI) treated by two-step austempering process were investigated. High Cu content in nodular cast irons leads to a significant volume fraction of retained austenite in the iron after austempering treatment, but the carbon content of austenite decreases with the increasing of Cu content. Moreover, austenitic stability reaches its maximum when the Cu content is 1.4% and then drops rapidly with further increase of Cu. The ultimate tensile strength and yield strength of the ADI firstly increases and then decreases with increasing the Cu content. The elongation keeps constant at 6.5% as the Cu content increases from 0.2% to 1.4%, and then increases rapidly to 10.0% with further increase Cu content to 2.0%. Impact toughness is enhanced with Cu increasing at first, and reaches a maximum 122.9 J at 1.4% Cu, then decreases with the further increase of Cu. The fracture toughness of ADI shows a constant increase with the increase of Cu content. The influencing mechanism of Cu on austempered ductile iron (ADI) can be classified into two aspects. On the one hand, Cu dissolves into the matrix and functions as solid solution strengthening. On the other hand, Cu reduces solubility of C in austenite and contributes more stable retained austenite.