Biologically inspired silk fibroin grafted polyacrylonitrile filtration membrane prepared in ZnCl_2 aqueous solution

摘要

In this study, biologically inspired silk fibroin grafted polyacrylonitrile(SF-g-PAN) filtration membrane was prepared using ZnCl_2 aqueous solution as solvent, avoiding the use of organic solvents. Phase inversion occurred when Zn^(2+)and Cl-ions gradually diffused into water, creating a well-connected ion channel network and the SF-g-PAN filtration membrane was obtained. The membranes were observed by SEM and 3D ultra-depth microscope. The hydrophilic property, pore size distribution and dye rejection of the membrane were investigated. Results showed that the membrane has no finger hole formation because ZnCl_2 aqueous solution has a lower curing rate parameter compared with organic solvents. SF-gPAN membrane possessed good anti-fouling properties and pH sensitivity. The pore size distribution of the SF-g-PAN membrane was 0.25–1.04 nm. The rejection of direct yellow 27(Mw = 662.6) and amaranth(Mw = 604.5) was 96.51% and 30.63%, with the flux of 72.32 L m^(-2) h^(-1) and 73.83 L m^(-2) h^(-1) respectively at0.1 MPa. The SF-g-PAN membrane has a wide range of applications prospect in fine separation, dye desalination, waste water treatment and biomedical fields.