IR-transparent MgO-Gd_(2)O_(3) composite ceramics produced by self-propagating high-temperature synthesis and spark plasma sintering

摘要

A glycine–nitrate self-propagating high-temperature synthesis(SHS)was developed to produce composite MgO-Gd_(2)O_(3) nanopowders.The X-ray powder diffraction(XRD)analysis confirmed the SHS-product consists of cubic MgO and Gd_(2)O_(3) phases with nanometer crystallite size and retains this structure after annealing at temperatures up to 1200°C.Near full dense high IR-transparent composite ceramics were fabricated by spark plasma sintering(SPS)at 1140°Cand 60 MPa.The in-line transmittance of 1 mm thick MgO-Gd_(2)O_(3) ceramics exceeded 70%in the range of 4–5 mm and reached a maximum of 77%at a wavelength of 5.3 mm.The measured microhardness HV0.5 of the MgO-Gd2O3 ceramics is 9.5±0.4 GPa,while the fracture toughness(KIC)amounted to 2.0±0.5МPa·m1/2.These characteristics demonstrate that obtained composite MgO-Gd_(2)O_(3) ceramic is a promising material for protective infra-red(IR)windows.