Determination of the orientation relations between the low- and high-temperature phases of NiS

摘要

In order to get information about the transition mechanism, the temperature-induced transformation in the binary compound NiS was investigated. Above 379 ℃, a single crystal of millerite β-NiS transforms to polycrystalline NiAs type α-NiS with a sharp texture. Pole figures of both phases in the same orientation were measured using synchrotron radiation and an imaging plate detector. The Rietveld texture analysis showed that there are at least three components of the high-temperature α-NiS phase. The main component shows the following orientation relations: [001]_(NiAs type)‖[001]_(millerite),[100]_(NiAs type)‖[210]_(millerite),[210]_(NiAs type)‖[100]_(millerite), The broad peaks of the recovered polycrystalline millerite occur at the same positions as the reflections of the original single crystal.