Creep behavior of a superplastic Y-TZP/Al_2O_3 composite: an examination of the possibility for diffusion creep

摘要

The creep characteristics of a high purity superplastic Y-TZP/Al_2O_3 composite were studied. The test damples had a uniform initial grain size of essentially equiaxed grains and the phase distribution was also uniform. Creep tests were conducted at elevated temperatures in tension an measurements were taken after testing to determine the average isze and shape of the grains. The creep curves showed the existence of a primary stage of creep and then a transition into a steady-state region where the strain rate remained reasonably constant. Observations by scanning e lectron microscopy revealed an elongation of the alumina grains with the grain strain essentially matching the overall strain within the sample. There was some grain grwoth after testing at the lower stresses. Preliminary observations using an atomic force microscope revealed direct evidence for the occurrence of some grain boundary sliding within the samples. The results are compared with earlier data reported for Y-TZP/A;_2O_3 composites and they are analyzed using the interface reaction-controlled diffusion creep model.