RESEARCH IN DETECTING CRACKS ON THE SURFACE OF CONTINUOUS CASTING SLABS

机译：连铸坯表面裂纹检测的研究

获取原文

获取原文并翻译 | 示例

页面导航

摘要
著录项
相似文献
相关主题

摘要

In Metal Rapid Forming and Manufacturing System of continuous casting, Wavelet Method and Fractal Geometry have been discussed to recognize patterns of flaws on the surface of continuous-casting slabs, and then to detect the flaws continuously.

机译：在连铸金属快速成形制造系统中，讨论了小波法和分形几何学，以识别连续铸造板坯表面的缺陷图案，然后连续检测缺陷。

著录项

来源
《Second International Conference on Rapid Prototyping amp; Manufacturing 2002 (ICRPM 2002): Progress in Rapid Prototyping and Papid Manufacturing Aug 19-20, 2002 Beijing, China》|2002年|p.478-479|共2页
会议地点 Beijing(CN);Beijing(CN)
作者
Xiaoming Yang; Guimei Hao; Youming Bi;
展开▼
作者单位

Taiyuan Heavy Machinery Institute, Taiyuan 030000, China;

展开▼
会议组织
原文格式 PDF
正文语种 eng
中图分类一般工业技术;
关键词
continuous-casting; crack detecting; wavelet-method;

机译：连铸；裂纹检测；小波方法;

相似文献

外文文献
中文文献
专利

1. Occurrence Mechanism and Prevention Method of Longitudinal Surface Cracks Near Slab Corner in Continuous Casting (Development of Variable Multi-Tapered Mold for High Speed Casting) [J] . Yoshiyuki MATOBA, Kazuo OKAMURA, Toshihiko MURAKAMI, JSME International Journal. Series A, Solid mechanics and material engineering . 2005,第3期

机译：连铸板坯拐角附近表面纵裂纹的产生机理及预防方法（高速铸造可变多锥模具的开发）
2. Occurrence Mechanism and Prevention Method of Longitudinal Surface Cracks Near Slab Corner in Continuous Casting (Development of Variable Multi-Tapered Mold for High Speed Casting) [J] . Yoshiyuki MATOBA, Kazuo OKAMURA, Toshihiko MURAKAMI, JSME International Journal. Series A, Solid mechanics and material engineering . 2005,第3期

机译：连铸板坯拐角附近表面纵裂纹的发生机理及预防方法（高速铸造可变多锥模具的开发）
3. Effect of cooling rate on the hot ductility of boron bearing steel during continuous casting (Study for prevention of corner crack on continuous casting slab) [J] . Kyungchul Cho, Yangmo Koo, Joongkil Park Journal of Korean Institute of Metal and Materials . 2008,第6期

机译：冷却速度对连铸过程中含硼钢热延展性的影响（防止连铸板角裂的研究）
4. RESEARCH IN DETECTING CRACKS ON THE SURFACE OF CONTINUOUS CASTING SLABS [C] . Xiaoming Yang, Guimei Hao, Youming Bi International conference on rapid prototyping manufacturing . 2002

机译：持续铸造板表面裂缝检测裂缝的研究
5. A model and data-based analysis of longitudinal surface cracking in the continuous casting of middle carbon steel slabs. [D] . Suni, Jaakko Paavo. 1991

机译：中碳钢板坯连铸纵向表面开裂的模型和基于数据的分析。
6. Influence of M-EMS on Fluid Flow and Initial Solidification in Slab Continuous Casting [O] . Guoliang Liu, Haibiao Lu, Bin Li, 2021

机译：M-EMS对板坯连续铸造流体流动和初始凝固的影响
7. Compression Test to Reveal Surface Crack Sensitivity between 700 and 1100.DEG.C. of Nb-bearing and High Ni Continuous Casting Slabs. [O] . Shi Shu Xie, Joo Dong Lee, U-Sok Yoon, 2002

机译：压缩测试以显示700和1100.deg.c的表面裂纹敏感性。 Nb轴承和高Ni连续铸造板。
8. Criteria for the Formation of Cracks during Continuous Casting of Special Steels. Cost 504 Casting Technology Project SF 3. Final Report 1988-91. [R] . Holappa, L., Louhenkilpi, S., Miettinen, J. 1991

机译：特种钢连铸过程中裂纹形成的标准。成本504铸造技术项目sF 3.最终报告1988-91。

RESEARCH IN DETECTING CRACKS ON THE SURFACE OF CONTINUOUS CASTING SLABS

摘要

著录项

相似文献

相关主题

期刊订阅